Iron Oxide-Activated Carbon Composites for Enhanced Microwave-Assisted Pyrolysis of Hardwood

Abstract

A commercial activated carbon (AC) was modified through iron oxide incorporation to obtain microwave absorbers (MWAs) for microwave-assisted pyrolysis. The influence of iron oxide content (5 and 20 wt% Fe3O4) and the modification methods were tested as follows: (1) in situ co-precipitation + washing step with Milli-Q; (2) in situ co-precipitation + washing step with Milli-Q/ethanol; and (3) physical iron oxide blending. The resulting MWAs were evaluated on the microwave-assisted pyrolysis of hardwood in a Milestone Flexiwave microwave reactor. The biochar yield varied from 24 wt% to 89 wt% and was influenced by the modification method rather than the iron oxide addition. The MWAs with physically blended iron oxide resulted in biochar yields comparable to conventional biochar (450 degrees C). Furthermore, the addition of iron oxide-activated carbon composites during the microwave-assisted pyrolysis caused a significant decrease in the biochar's 16 EPA polycyclic aromatic hydrocarbons, mainly by reducing the am